Article

Understanding Composite Compression Test Methods

John Moylan

By Engaged Expert

John Moylan

More content from this author

Learn about our Engaged Experts

John Moylan is a senior expert in the testing of polymer based composite mater/nucleus/2020/composite-compression-test-methods/ials for the global Aerospace sector.

Compression properties of composites are impacted by the resin and fiber resin interface, and often determine the overall design, size, and weight of a part. Composite compression testing is cruc/nucleus/2020/composite-compression-test-methods/ial for screening new mater/nucleus/2020/composite-compression-test-methods/ials and maintaining quality control.   

The goal of a composite compression test is to drive compressive forces into a uniform gauge area without causing premature failure or improper failure modes in other parts of the specimen. As composite mater/nucleus/2020/composite-compression-test-methods/ials continue to become more advanced, obtaining a universal standard for performing compression testing has presented challenges.  

Composite testing often follows ASTM or ISO methods, but organizations sometimes develop proprietary test methods. The various techniques may present differing results, so careful documentation of the test method and outcome is cruc/nucleus/2020/composite-compression-test-methods/ial in understanding the mater/nucleus/2020/composite-compression-test-methods/ial properties. 

The existing composite compression test methods fall into three classes, depending on how mater/nucleus/2020/composite-compression-test-methods/ials are loaded on the test frame:

  • Bending
  • Shear
  • End-loaded

 

ASTM Bend composite compression test 

ASTM D5467 and ASTM D7249 document two of the most common bending test methods for compressive properties of composites. 

Bend loading utilizes a sandwich beam construct for testing, where one face is in compression, and the opposite face is in tension. The compressive face is generally constructed with a thinner facesheet so that the beam fails first in compression. 

When constructing the specimen, spans, core mater/nucleus/2020/composite-compression-test-methods/ial, thickness, and adhesives are selected to ensure that the correct failure mode (compression facing) is achieved. Strain gauges on the compressive face are used to measure modulus, Poisson’s ratio, and strain to failure.  

 

Shear loaded compression testing ASTM D3410

Some methods apply a shear load to the gauge area of the specimen. One of the first methods, commonly called Celanese compression, loads the sample through wedges that are gripped by a cone-shaped fixture. The specimens are rectangular and usually tabbed. Celanese compression was init/nucleus/2020/composite-compression-test-methods/ially referred to in the ASTM D3410 standard but has since been removed. The Celanese specimens were generally limited to 0.25” in width by the ASTM Standard and 10mm by ISO 14126.  The overall length is 5.5 inches with a 0.5” unsupported length. 

Though Celanese compression is generally considered obsolete, it is sometimes requested to compare to historical data. For this method, mater/nucleus/2020/composite-compression-test-methods/ial thickness is a critical consideration and must be within the narrow range specified, which allows proper seating of the wedges with the cones. 

The current version of ASTM D3410 is commonly called the IITRI method, which was developed to mitigate some of the weaknesses in the Celanese method. The IITRI fixture is large and heavy, which presents challenges when used at extreme temperatures. Specimens used for this method may be up to 1 inch wide and 5.5 inches long with 0.5 inches of unsupported length. The wedges are loading through a rectangular seat, so the overall thickness of the specimen is not as critical as in the Celanese method. However, the mater/nucleus/2020/composite-compression-test-methods/ial within the gauge area must be thick enough to preclude Euler buckling. Most data users agree that the test provides a compressive stress result because of the significant unsupported length in the mater/nucleus/2020/composite-compression-test-methods/ial. 

 

End-loading compression testing ASTM D695

Plastics have traditionally been tested using the end loading methods described in ASTM D695. This method allows for the end-loading of a prism that is square or round in cross-section. A dog-bone shaped flat specimen may also be used and is loaded in a side support fixture that precludes buckling.   

The Suppliers of Advanced Composites Mater/nucleus/2020/composite-compression-test-methods/ials Assoc/nucleus/2020/composite-compression-test-methods/iation, SACMA, adopted and formalized an industry practice of using tabbed specimens with a 0.188-inch gauge length. The samples generally result in a higher apparent compressive strength because of the shorter gauge length. Since all these specimens are end-loaded, the ends must be flat and parallel for relevant results. If the specimens fail or broom at the ends, the results should be considered invalid.  

Additionally, if the level of torque applied to the bolts that secure specimen to the fixture is too high, test results may be invalid. Due to the short gauge length and the var/nucleus/2020/composite-compression-test-methods/iability of friction from the side support fixture, further standardization of this method has been slow.   

 

Combination of shear and end-loading compression testing ASTM D6641

Continued fixture development resulted in a combined loading compression fixture. ASTM D6641 describes the appropr/nucleus/2020/composite-compression-test-methods/iate fixture and test method. 
Like the earlier methods, the nominal specimen is 5.5 inches long with a 0.5 inch of unsupported length. By clamping the ends of the fixture between square ends, the specimen is loaded with a combination of end and shear loading. 

The combined loading compression fixture is smaller and easier to use than the IITRI fixture. Carefully torquing the fixture bolts to an even, specified level is essent/nucleus/2020/composite-compression-test-methods/ial. Specimens are strain gauged with back-to-back gauges to monitor for Euler buckling. The percent bending is reported with the test data and may be used to troubleshoot anomalous data.

For composite design, values for compression with a hole to simulate a stress riser is often needed. Open hole compression test ASTM D6484 is such a method for obtaining those values.

Comparison of composite compression test methods 

Test

Nominal Specimen

Unsupported gauge length

Critical Parameters

Comments

ASTM D5467 & D7249

24” X 1” bonded to a sandwich beam

0”

Specimen uniformity

Expensive specimen to fabricate and rarely used.

ASTM D3410 (IITRI)

5.5” X 1”

0.5”

Symmetry of Tabs

Large, heavy fixture

ASTM D695

3.13” X 0.5” dogbone

0”

End flatness

For woven mater/nucleus/2020/composite-compression-test-methods/ials only

SACMA SRM 1R-94

3.13” X 0.5” tabbed

0.188”

End flatness, fixture torque

Provides higher relative values

ASTM D6641

5.5” X 0.5” or 1”

0.5”

End flatness, fixture torque

Most common method, has unsupported length and is easier to use

 

Conclusion 

Composite compression testing methods vary by fixture design, loading techniques, and specimen size. While there is no set standard for testing the compressive strength of composites, our experts can help you select the test methods that will generate the required result. Element works diligently to make certain your composite mater/nucleus/2020/composite-compression-test-methods/ials are fit for purpose.

If you require composite compression testing or have questions about which methods are right for your mater/nucleus/2020/composite-compression-test-methods/ial, please contact us today